Our S-30 is an established industry standard. One of the finest waterborne polymer based treatment systems available. The special resins allow the polymers to saturate concrete and embed a dense, high compressive membrane.
One of the longest pit-lives available, with easy workability and with excellent compatibility with cement primers, adhesives and flooring products.
Meets LEED EQ requirements and provides very low perm rates per ASTM E96. Controls up to 30 lbs MVER and 100% RH.
USES: Remedial only
Synthetic30 is a water-based high performance treatment for concrete surfaces requiring drastic moisture reduction. The product offers the below benifits:
0.0 to 10 pounds & RH 100%……….1 coat @ 200 ft / gallon/ coat
10.1 to 15 pounds & RH 100%……..1 coat @ 160 ft / gallon/ coat
15.1 to 30 pounds & RH 100%……..2 coats @ 250 ft / gallon/ coat
Substrates with excessive cracking will require additional product to treat cracks and joints prior to covering product with any type of flooring or coating system. Approximate vapor emission rate after application: 1.0 to 2.0 lbs. per ASTM F1869. Coverage rates may vary based on concrete profile and porosity. Product is resistant to 14pH for all spread rates.
Cracks and joints that are less than 1/8 inch wide may be sealed with Synthetic30 during application. Reseal cracks that remain exposed after application with additional product for greater crack bridging.
Allow Synthetic30 to cure a minimum of 12 hours (80°F) – 24 hours (55°F) before using cement products to smooth uneven floor transitions. Use a high quality patch or Portland cement-based product only. A non-porous primer must be used to secure cement products. Do not use cement products with special additives as a replacement for a non-porous primer. Follow the flooring manufactures recommendations for cement thickness requirements.
Do not apply to concrete surfaces when temperatures are expected to fall below 45°F (7.2°C) during and 24 hours after application. Do not apply if rain, snow or dew point is expected prior to, during or after 24 hours of application. The concrete surface requires a shot-blasted profile and rough texture to allow maximum product penetration. Adhesion testing is recommended on previous sealed concrete.
Synthetics International manufactures and remains the exclusive distributor of Synthetic30 worldwide. The product is manufactured in the United States and is shipped as non-hazardous throughout the United States.
Clean equipment, drips and over-sprays with water while still wet. Dried product requires mechanical abrasion for removal.
Factory sealed units are packaged in 2 and 5 gallon Part A and Part B kits. Do not mix partial units.
Product may be stored and considered useable within one year of shipment.
| Synthetics30 | Control | |
|---|---|---|
| Grains/ ft2/ hour | 0.6 | 12.4 |
| Pounds/1000 ft2/ 24 hrs. | 2.0 | 42.4* |
| Grams/h·m2 | 0.4 | 8.6 |
*Testing based on concrete with extremely excessive water vapor emision of 42.2 lbs. Results in a 95% moisture reduction vs. uncoated samples.
| Synthetics30 | Control | |
|---|---|---|
| Perm (inch-pound) | 1.4 | 30.2* |
| Grams/Pa·s·m2 x 10-8 | 8.1 | 172.8 |
| Nanograms/ Pa·s·m2 | 81.1 | 1728.2 |
Core#1 – 275psi (100% concrete cohesive failure)
Core#2 – 225psi (100% concrete cohesive failure)
Core#3 – 375psi (100% concrete cohesive failure)
Core#4 – 325psi (100% concrete cohesive failure)
Core#5 – 350psi (100% concrete cohesive failure)
Alkali of 14pH – 100% Resistant to exposure
35% Potassium Hydroxide – 100% Resistant to exposure
Density: 1.1766 g/ml
VOC: 62 g/liter (0.52 lbs/gal)
Standard Classroom & Office Space: Pass
No Formaldehyde or other CREL VOCs detected
California High Performance Schools EQ Credit 2.2
LEED New Construction & Major Renovations, Ver 2.2
EQ Credit 4.2: Low-Emitting Materials: Coatings
LEED Schools for New Construction and Major Ren.
EQ Credit 4: Low-Emitting Materials
Complies with VOC restrictions in all regions. Actual Mixed VOC = 62g/L (0.52 lbs/gal)